Study of tapping process of carbon fiber reinforced plastic composites/AA7075 stacks

The present investigation aims at studying the tapping process of a three-layer stack constituted by two CFRP layers and a core plate in AA7075 aluminum alloy. The CFRP laminates were obtained by a pre-impregnated woven sample made up of T700 carbon fibers and a thermoset epoxy matrix. Tapping experiments were performed on a 5-axis machining center instrumented with a dynamometer to measure thrust force generated during process. A high-speed steel tool, coated with nanocomposite TiAlN, was used. According to the tool manufacturer recommendations, rotational speed and feed rate were 800 rpm and 1000 mm/min, respectively. Similar thrust force time history responses were obtained by tapping different holes, even though the vertical force increases with number of threaded holes. Furthermore, a quantitative evaluation of delamination at the periphery of entry holes was carried out. The delamination at the entry hole strongly increases with number of threaded holes.